Influence of accelerated curing on the compressive strength of polymer-modified concrete

In recent building practice, rapid construction is one of the principal requisites. Furthermore, in designing concrete structures, compressive strength is the most significant of all parameters. While 3-d and 7-d compressive strength reflects the strengths at early phases, the ultimate strength is paramount. An effort has been made in this study to develop mathematical models for predicting compressive strength of concrete incorporating ethylene vinyl acetate (EVA) at the later phases. Kolmogorov-Smirnov (KS) goodness-of-fit test was used to examine distribution of the data. The compressive strength of EVA-modified concrete was studied by incorporating various concentrations of EVA as an admixture and by testing at ages of 28, 56, 90, 120, 210, and 365 d. An accelerated compressive strength at 3.5 hours was considered as a reference strength on the basis of which all the specified strengths were predicted by means of linear regression fit. Based on the results of KS goodness-of-fit test, it was concluded that KS test statistics value (D) in each case was lower than the critical value 0.521 for a significance level of 0.05, which demonstrated that the data was normally distributed. Based on the results of compressive strength test, it was concluded that the strength of EVA-modified specimens increased at all ages and the optimum dosage of EVA was achieved at 16% concentration. Furthermore, it was concluded that predicted compressive strength values lies within a 6% difference from the actual strength values for all the mixes, which indicates the practicability of the regression equations. This research work may help in understanding the role of EVA as a viable material in polymer-based cement composites.     

Deacetylated Cellulose Acetate/Polyurethane Composite Nanofiber Membranes with Highly Efficient Oil/Water Separation and Excellent Mechanical Properties

Nowadays, oil pollution has become more serious, which causes great threats both to the ecological environment and human life. In this study, a novel type of multifunctional deacetylated cellulose acetate/polyurethane (d-M_CA:M_TPU) composite nanofiber membranes for oil/water separation are successfully fabricated by electrospinning, which show super-amphiphilicity in air, super-hydrophilicity in oil, and oleophobicity in water. All the d-M_CA:M_TPU composite nanofiber membranes with different mass ratios can be used as water-removing, oil-removing, and emulsion separation substance only by gravity driving force. The highest separation flux for water and oil reaches up to 37 000 and 74 000 L m⁻² h⁻¹, respectively, and all the separation efficiencies are more than 99%. They have outstanding comprehensive mechanics performance, which can be controlled by simply adjusting the mass ratios. They show excellent antifouling and self-cleaning ability, endowing powerful cyclic stability and reusability. Those results show that d-M_CA:M_TPU composite nanofiber membranes have great application prospects in oil/water separation.     

Effect of cellulose acetate/cellulose triacetate ratio on reverse osmosis blend membrane performance

Surface functionalization and modification including the grafting process are effective approaches to improve and enhance the reverse osmosis (RO) membrane performance. This work is aimed to synthesize grafted/crosslinked cellulose acetate (CA)/cellulose triacetate (CTA) blend RO membranes using N-isopropylacrylamide (N-IPAAm) as a monomer and N,N-methylene bisacrylamide (MBAAm) as a crosslinker. The morphology of these membranes was analyzed by scanning electron microscopy and their surface roughness was characterized by atomic force microscopy. The performance of these membranes was evaluated through measuring two major parameters of salt rejection and water flux using RO unit at variable operating pressures. It was noted that the surface average roughness obviously decreased from 148 nm for the pure CA/CTA blend membrane with 2.5% CTA to 110 nm and 87 nm for the grafted N-IPAAm and grafted/crosslinked N-IPAAM/MBAAm/CA/CTA-RO membranes, respectively. Moreover, the contact angle decreased from 51.98° to 47.6° and 43.8° after the grafting and crosslinking process. The salt rejection of the grafted CA/CTA-RO membrane by 0.1% N-IPAAm produced the highest value of 98.12% and the water flux was 3.29 L/m²h at 10 bar.     

P(DBF-VA)型柴油低温流动性改进剂的研制

针对新疆地产柴油蜡含量较高的特点,以游离基聚合法合成了富马酸双链混合酯和醋酸乙烯酯共聚物型[P(DBF-VA)]柴油低温流动改进剂,利用正交实验研究了单体配比,引发剂用量,溶剂用量,聚合温度对聚合物降冷滤效果的影响。共聚物用IR进行表征,利用XRD初步探讨了该降凝剂的降凝机理。结果表明:该剂能使吐哈—10~#、0~#柴油冷滤点降低10℃和7℃;使独山子0~#柴油冷滤点下降12℃;使石化0~#柴油冷滤点下降8℃;使克拉玛依0~#柴油的冷滤点下降8℃。     

甲醇气相羰化合成醋酸甲酯的产物分析

以热导池为检测器,分别采用8/100间苯二甲酸+GDX-103、Porapak-Q分析甲醇气相羰化的液相产物和气相产物,确定了气相色谱分析的操作条件,测定了各组分的校正因子,并应用于甲醇绿色羰化合成醋酸甲酯的催化剂评选,得到了满意的结果。     

Valorisation of waste fractions from autohydrolysis of selected lignocellulosic materials

Non‐isothermal processing of lignocellulosic materials in aqueous media (autohydrolysis reaction) under mild conditions leads to solutions containing valuable chemicals (oligosaccharides, sugars and acetic acid) and other, undesired, compounds (belonging to the extractive and acid‐soluble lignin fractions) which have to be removed in further purification treatments. Liquors obtained by non‐isothermal autohydrolysis of Eucalyptus globulus wood and corncobs under a variety of operational conditions were extracted with ethyl acetate in order to remove non‐saccharide components, and the suitability of the fraction dissolved in the organic phase was assayed for possible utilisation as an antioxidant. The yield and antioxidant activity of ethyl acetate extracts (measured by the α,α‐diphenyl‐β‐picrylhydrazyl (DPPH) radical scavenging capacity) showed a strong dependence on the autohydrolysis conditions. The antioxidant activity of extracts obtained under selected operational conditions compared well with synthetic antioxidants. © 2003 Society of Chemical Industry     

KOAc/NaY催化合成邻甲基苯甲醚

以KOA c/NaY为催化剂,在连续流动固定床反应器内,邻甲基苯酚(OC)与碳酸二甲酯(DMC)经过气固相催化反应合成了邻甲基苯甲醚(OM)。考察了内、外扩散对KOA c/NaY催化剂活性的影响。实验结果表明,当气流线速度大于30cm/m in时可消除外扩散对合成反应的影响;当KOA c/NaY催化剂的平均粒径在0.30~0.75mm(20~80目的颗粒)时能消除内扩散对合成反应的影响。在消除内、外扩散效应后,还考察了反应温度、原料配比、空速对合成反应的影响,得到较佳的反应条件:催化剂5mL,反应温度548K,反应压力0.6M Pa,空速0.6h-1,n(DMC)∶n(OC)=1,在线评价时间7h。在此条件下,OC的转化率高达85.7%,OM的选择性大于99%。     

由乙腈一步法制备乙酸丁酯的研究

以丁醇和制备丙烯腈的副产物乙腈为原料 ,采用一步法合成了乙酸丁酯。通过正交实验得到了影响反应的 4种因素。确定了最佳的工艺条件为 :催化剂的量为样品质量的 40 % ;n(CH3CN)∶ n(C4 H9OH) =1∶ 1 .0 5 ;反应温度为 1 0 5℃ ;反应时间为 8h。在此反应条件下 ,乙酸丁酯的收率为 88.8% ,纯度可达 99.5 %。并用气相色谱及红外光谱对产品的纯度进行了表征     

驱蚊酯的合成及应用研究

本文合成了一种高效低毒驱蚊剂-驱蚊酯[(insectifuge ester)[1],3-(Acetyl-butyl-amino)-propionic acid ethyl ester],并对其结构进行了全面鉴定,同时对其合成过程中所产生的副产物进行了分析测定。用驱蚊酯配成含2.3%驱蚊酯的花露水,并测试了其驱蚊效果,有效驱蚊时间可达5小时以上。